| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |
| Particle Size | 6 Microns |
|---|---|
| Purity | 99.99% |
| Application Temperature | Up To 3000°C |
| Thermal Conductivity | 125 W/mK |
| Density | 1.85 G/cm3 |
| Particle Size | 6 Microns |
|---|---|
| Purity | 99.99% |
| Application Temperature | Up To 3000°C |
| Thermal Conductivity | 125 W/mK |
| Density | 1.85 G/cm3 |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 500/50 PPM |
| Compressive Strength | 175 MPa |
|---|---|
| Hardness | 65 HS |
| Density | 2.72 G/cm3 |
| Color | Metallic Grey |
| Material | Copper And Graphite |
| Bulk Density | 1.72 G/cm3 |
|---|---|
| Compressive Strength | 85 Mpa |
| Flexural Strength | 42 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 60 HSD |
| Particle Size | 6 Microns |
|---|---|
| Purity | 99.99% |
| Application Temperature | Up To 3000°C |
| Thermal Conductivity | 125 W/mK |
| Density | 1.85 G/cm3 |
| Flexural Strength | 50 MPa |
|---|---|
| Thermal Conductivity | 105 W/mK |
| Density | 1.81 G/cm3 |
| Purity | 99.95% |
| Thermal Expansion Coefficient | 5.4 X 10^-6 /K |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Bulk Density | 1.78 G/cm3 |
|---|---|
| Compressive Strength | 85 Mpa |
| Flexural Strength | 45 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |