| Flexural Strength | 50 MPa |
|---|---|
| Thermal Conductivity | 105 W/mK |
| Density | 1.81 G/cm3 |
| Purity | 99.95% |
| Thermal Expansion Coefficient | 5.4 X 10^-6 /K |
| Bulk Density | 1.78 G/cm3 |
|---|---|
| Compressive Strength | 105 Mpa |
| Flexural Strength | 52 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 65 HSD |
| Corrosion Resistance | Excellent |
|---|---|
| Purity | 99.95% |
| Chemical Resistance | High |
| Thermal Conductivity | 105 W/mK |
| Applications | Crucibles, Refractories, Foundry Coatings |
| Bulk Density | 1.85 G/cm3 |
|---|---|
| Compressive Strength | 115 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 10~13 µΩ.m |
| Shore Hardness | 65 HSD |
| Bulk Density | 1.90 G/cm3 |
|---|---|
| Compressive Strength | 135 Mpa |
| Flexural Strength | 70 Mpa |
| Electric Resistance | 13~15 µΩ.m |
| Shore Hardness | 75 HSD |
| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |
| Particle Size | 6 Microns |
|---|---|
| Purity | 99.99% |
| Application Temperature | Up To 3000°C |
| Thermal Conductivity | 125 W/mK |
| Density | 1.85 G/cm3 |
| Particle Size | 6 Microns |
|---|---|
| Purity | 99.99% |
| Application Temperature | Up To 3000°C |
| Thermal Conductivity | 125 W/mK |
| Density | 1.85 G/cm3 |
| Density | 1.85g/cm3 |
|---|---|
| Particle Size | 12 Microns |
| Mechanical Strength | High |
| Porosity | Low |
| Thermal Conductivity | 110 W/mK |
| Flexural Strength | 50 MPa |
|---|---|
| Thermal Conductivity | 105 W/mK |
| Density | 1.81 G/cm3 |
| Purity | 99.95% |
| Thermal Expansion Coefficient | 5.4 X 10^-6 /K |