| Bulk Density | 1.78 G/cm3 |
|---|---|
| Compressive Strength | 105 Mpa |
| Flexural Strength | 52 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 65 HSD |
| Particle Size | 6 Microns |
|---|---|
| Purity | 99.99% |
| Application Temperature | Up To 3000°C |
| Thermal Conductivity | 125 W/mK |
| Density | 1.85 G/cm3 |
| Bulk Density | 1.85 G/cm3 |
|---|---|
| Compressive Strength | 105 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 65 HSD |
| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |
| Dimensional Stability | Excellent |
|---|---|
| Color | Dark Grey |
| Surface Finish | Smooth |
| Melting Point | 3650°C |
| Advantages | High Precision, Good Surface Finish, Long Tool Life |
| Dimensional Stability | Excellent |
|---|---|
| Color | Dark Grey |
| Surface Finish | Smooth |
| Melting Point | 3650°C |
| Advantages | High Precision, Good Surface Finish, Long Tool Life |
| Bulk Density | 1.85 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 65 HSD |
| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |
| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 115 Mpa |
| Flexural Strength | 60 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |