| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 500/50 PPM |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Melting Point | 3652°C |
|---|---|
| Purity | 99.9% |
| Shape | Powder |
| Material | Graphite |
| Hardness | 75 HS |
| Product Type | Graphite |
|---|---|
| Application | Photovoltaic (Solar) |
| Color | Black |
| Electrical Conductivity | 100 W/m.k |
| Melting Point | 3652°C |
| Customization | Available |
|---|---|
| Application | Heating Elements For Industrial Furnaces |
| Density | 1.7-1.9 G/cm3 |
| Maximum Operating Temperature | 3000℃ |
| Material | Graphite |
| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |
| Thermal Conductivity | 130 W/m·K |
|---|---|
| Corrosion Resistance | Excellent |
| Color | Black |
| Thermal Expansion Coefficient | 4.8 X 10^-6 /K |
| Density | 1.7 G/cm³ |
| Thermal Conductivity | 130 W/m·K |
|---|---|
| Corrosion Resistance | Excellent |
| Color | Black |
| Thermal Expansion Coefficient | 4.8 X 10^-6 /K |
| Density | 1.7 G/cm³ |