| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Density | 1.85g/cm3 |
|---|---|
| Particle Size | 12 Microns |
| Mechanical Strength | High |
| Porosity | Low |
| Thermal Conductivity | 110 W/mK |
| Flexural Strength | 50 MPa |
|---|---|
| Thermal Conductivity | 105 W/mK |
| Density | 1.81 G/cm3 |
| Purity | 99.95% |
| Thermal Expansion Coefficient | 5.4 X 10^-6 /K |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Bulk Density | 1.78 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 10~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 500/50 PPM |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 500/50 PPM |