| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Customization | Available |
|---|---|
| Application | Heating Elements For Industrial Furnaces |
| Density | 1.7-1.9 G/cm3 |
| Maximum Operating Temperature | 3000℃ |
| Material | Graphite |
| Density | 1.85g/cm3 |
|---|---|
| Particle Size | 12 Microns |
| Mechanical Strength | High |
| Porosity | Low |
| Thermal Conductivity | 110 W/mK |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Bulk Density | 1.85 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 65 HSD |