| Bulk Density | 1.85 G/cm3 |
|---|---|
| Compressive Strength | 105 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 65 HSD |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Bulk Density | 1.80 G/cm3 |
|---|---|
| Compressive Strength | 100 Mpa |
| Flexural Strength | 50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Shore Hardness | 60 HSD |
| Thermal Conductivity | 110-125W/mK |
|---|---|
| Porosity | 12-15% |
| Flexural Strength | 60 MPa |
| Coefficient Of Thermal Expansion | 5.2 X 10^-6 /K |
| Density | 1.85 G/cm3 |
| Bulk Density | 1.76-1.80 G/cm3 |
|---|---|
| Compressive Strength | 85-95 Mpa |
| Flexural Strength | 45-50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 50 PPM |
| Bulk Density | 1.76-1.80 G/cm3 |
|---|---|
| Compressive Strength | 85-95 Mpa |
| Flexural Strength | 45-50 Mpa |
| Electric Resistance | 11~13 µΩ.m |
| Ash Content | 50 PPM |
| Bulk Density | 1.82 G/cm3 |
|---|---|
| Compressive Strength | 110 Mpa |
| Flexural Strength | 55 Mpa |
| Electric Resistance | 13~14 µΩ.m |
| Shore Hardness | 68 HSD |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |
| Application | Lithium Battery Anode Material |
|---|---|
| Particle Size | 12 μm |
| Compressive Strength | 100 MPa |
| Purity | 99.95% |
| Flexural Strength | 50 MPa |